Desiccant Masterbatch Parameter Table
Defoamer(disiccant) masterbatch can be widely used in plastic products made with recycled PP/PE materials. Its main component is CaO. Defoamer masterbatch can effectively absorb the moisture in the material, so as to avoid bubbles, moire, cracks and so on caused by moisture. The adding ratio of the defoamer masterbatch is 2% to 5%.
Following is ourparameter table:
PRODUCT NAME: Plastic desiccant masterbatch
|
SUITABLE PRODUCT FOR: RECYCLED PLASTIC FILMS, EXTRUSION, INJECTION, etc. |
SUGGESTED ADD RATIO: Recommend to add 2.0% - 4.0% |
OBSERVATION: The masterbatch dosage is according to the final product requirements. |
PROPERTIES | STANDARD | RANGE |
CARRIER RESIN | / | PE/PP |
ORIGIN | / | SHANDONG,CHINA |
PELLET SHAPE & SIZE | / | 2.5mm-3mm Pellet |
COLOR | / | White, Grey, Black |
FILLER(CaO) | CAS NO. | 1305-78-8 |
POLYMER | CAS NO. | 9002-88-4 |
ADDITIVE | CAS NO. | 110-30-5 |
CaO CONTENT | % | 75%-88% |
FILLER CONTENT | % | 0 |
VOLATILITY | / | 1.5%±0.5% |
MELTING POINT | ISO11357:1999 | 120℃-150℃ |
MOISTURE ABSORBENT WEIGHT | ASTM D 570 | 20%-25% |
MFI 190℃/5KGS | ASTM D 1238 | 1-10g/10min |
DENSITY | ASTM D 792 | 1.5-1.9g/cm3 |
PACKAGE | / | 5kg per bag,25kg/ctn |
DELIVERY TIME | / | Less than 7 days |
MOQ | / | 1 Tons |
STORAGE | Keep the products in a dry, ventilated place, Note to avoid moisture and insolation, rain and breakage in transportation. |